Reducing reactions between polysilicon gate electrodes and high dielectric constant gate dielectrics

ABSTRACT

In a metal gate replacement process, a gate electrode stack may be formed of a dielectric covered by a sacrificial metal layer covered by a polysilicon gate electrode. In subsequent processing of the source/drains, high temperature steps may be utilized. The sacrificial metal layer prevents reactions between the polysilicon gate electrode and the underlying high dielectric constant dielectric. As a result, adverse consequences of the reaction between the polysilicon and the high dielectric constant dielectric material can be reduced.

BACKGROUND

The present invention relates to methods for making semiconductor devices, in particular, semiconductor devices with metal gate electrodes.

MOS field-effect transistors with very thin gate dielectrics made from silicon dioxide may experience unacceptable gate leakage currents. Forming the gate dielectric from certain high dielectric constant (K) dielectric materials, instead of silicon dioxide, can reduce gate leakage. As used herein, high-k dielectric means having a dielectric constant higher than 10. When, however, a high-k dielectric film is initially formed, it may have a slightly imperfect molecular structure. To repair such a film, it may be necessary to anneal it at a relatively high temperature.

Because such a high-k dielectric layer may not be compatible with polysilicon, it may be desirable to use metal gate electrodes in devices that include high-k gate dielectrics. When making a CMOS device that includes metal gate electrodes, it may be necessary to make the NMOS and PMOS gate electrodes from different materials. A replacement gate process may be used to form gate electrodes from different metals. In that process, a first polysilicon layer, bracketed by a pair of spacers, is removed selectively to a second polysilicon layer to create a trench between the spacers. The trench is filled with a first metal. The second polysilicon layer is then removed, and replaced with a second metal that differs from the first metal.

If in such a replacement gate process a high-k dielectric layer is formed after a polysilicon layer is removed, it may not be possible to apply a high temperature anneal to the high-k dielectric layer. It may not be possible to apply such an anneal to such a layer if a silicide has been formed on the transistor's source and drain regions prior to polysilicon layer removal. In addition, such an anneal may not be feasible if a high temperature intolerant metal has been formed on a first high-k dielectric layer prior to depositing a second high-k dielectric layer. For example, if a high temperature intolerant metal has been deposited on a first high-k dielectric layer to form the gate electrode for an NMOS transistor, then a high temperature anneal cannot be applied to a subsequently deposited second high-k dielectric layer, which will form the gate dielectric for the PMOS transistor.

BRIEF DESCRIPTION OF THE DRAWINGS

FIGS. 1A-1N represent cross-sections of structures that may be formed when carrying out an embodiment of the method of the present invention.

Features shown in these figures are not intended to be drawn to scale.

DETAILED DESCRIPTION

A method for making a semiconductor device is described. That method comprises forming a high-k (a dielectric constant greater than 10) gate dielectric layer on a substrate, and forming a sacrificial layer on the high-k gate dielectric layer. After etching the sacrificial layer and the high-k gate dielectric layer to form a patterned sacrificial layer and a patterned high-k gate dielectric layer, first and second spacers are formed on opposite sides of the patterned sacrificial layer. The patterned sacrificial layer is then removed to expose the patterned high-k gate dielectric layer and to generate a trench that is positioned between the first and second spacers. A metal layer is then formed on the high-k gate dielectric layer.

FIGS. 1A-1N illustrate structures that may be formed, when carrying out an embodiment of the method of the present invention. Initially, high-k gate dielectric layer 170 and a sacrificial metal layer 169 are formed on substrate 100, generating the FIG. 1A structure. Substrate 100 may comprise a bulk silicon or silicon-on-insulator substructure. Alternatively, substrate 100 may comprise other materials—which may or may not be combined with silicon—such as: germanium, indium antimonide, lead telluride, indium arsenide, indium phosphide, gallium arsenide, or gallium antimonide. Although a few examples of materials from which substrate 100 may be formed are described here, any material that may serve as a foundation upon which a semiconductor device may be built falls within the spirit and scope of the present invention.

Some of the materials that may be used to make high-k gate dielectric layer 170 include: hafnium oxide, hafnium silicon oxide, lanthanum oxide, zirconium oxide, zirconium silicon oxide, tantalum oxide, titanium oxide, barium strontium titanium oxide, barium titanium oxide, strontium titanium oxide, yttrium oxide, aluminum oxide, lead scandium tantalum oxide, and lead zinc niobate. Particularly preferred are hafnium oxide, zirconium oxide, titanium oxide and aluminum oxide. Although a few examples of materials that may be used to form high-k gate dielectric layer 170 are described here, that layer may be made from other materials that serve to reduce gate leakage. The layer 170 has a dielectric constant higher than 10 and from 15 to 25 in one embodiment of the present invention.

High-k gate dielectric layer 170 may be formed on substrate 100 using a conventional deposition method, e.g., a conventional chemical vapor deposition (“CVD”), low pressure CVD, or physical vapor deposition (“PVD”) process. Preferably, a conventional atomic layer CVD process is used. In such a process, a metal oxide precursor (e.g., a metal chloride) and steam may be fed at selected flow rates into a CVD reactor, which is then operated at a selected temperature and pressure to generate an atomically smooth interface between substrate 100 and high-k gate dielectric layer 170. The CVD reactor should be operated long enough to form a layer with the desired thickness. In most applications, high-k gate dielectric layer 170 may be less than about 60 Angstroms thick, for example, and, in one embodiment, between about 5 Angstroms and about 40 Angstroms thick.

A sacrificial metal layer 169 may be formed over the dielectric layer 170. The sacrificial metal layer 169 may be any metal that is capable of withstanding high temperatures (greater than 450° C.) without reaction with overlying polysilicon materials. As one example, the sacrificial metal layer 14 may be formed of titanium nitride. In one embodiment, the layer 169 may be formed by sputtering. In another embodiment, the layer 169 may be formed by atomic layer deposition.

After high-k gate dielectric layer 170 and sacrificial metal layer 169 are formed on substrate 100, sacrificial layer 171 is formed on high-k gate dielectric layer 170. In this embodiment, hard mask layer 172 is then formed on sacrificial layer 171, generating the FIG. 1B structure. Sacrificial layer 171 may comprise polysilicon and may be deposited on sacrificial metal layer 169 using a conventional deposition process. Sacrificial layer 171 may be, for example, between about 100 and about 2,000 Angstroms thick, and, in one embodiment, between about 500 and about 1,600 Angstroms thick.

Hard mask layer 172 may comprise silicon nitride between about 100 and about 1000 Angstroms thick, for example, and between about 200 and about 350 Angstroms thick in one-embodiment. Hard mask layer 172 may be formed on sacrificial layer 171.

Sacrificial layer 171 and hard mask layer 172 are then patterned to form patterned hard mask layers 130, 131, and patterned sacrificial layers 104, 106, and 169—as FIG. 1C illustrates. Conventional wet or dry etch processes may be used to remove unprotected parts of hard mask layer 172, sacrificial metal layer 169 and sacrificial layer 171. In this embodiment, after those layers have been etched, exposed part 174 of high-k gate dielectric layer 170 is removed.

Although exposed part 174 of high-k gate dielectric layer 170 may be removed using dry or wet etch techniques, it may be difficult to etch that layer using such processes without adversely affecting adjacent structures. It may be difficult to etch high-k gate dielectric layer 170 selectively to the underlying substrate using a dry etch process, and wet etch techniques may etch high-k gate dielectric layer 170 isotropically—undercutting overlying sacrificial layers 104, 106 in an undesirable fashion.

To reduce the lateral removal of high-k gate dielectric layer 170, as exposed part 174 of that layer is etched, exposed part 174 of high-k gate dielectric layer 170 may be modified to facilitate its removal selectively to covered part 175 of that layer. Exposed part 174 may be modified by adding impurities to that part of high-k gate dielectric layer 170 after sacrificial layer 171 has been etched. A plasma enhanced chemical vapor deposition (“PECVD”) process may be used to add impurities to exposed part 174 of high-k gate dielectric layer 170. In such a PECVD process, a halogen or halide gas (or a combination of such gases) may be fed into a reactor prior to striking a plasma. The reactor should be operated under the appropriate conditions (e.g., temperature, pressure, radio frequency, and power) for a sufficient time to modify exposed part 174 to ensure that it may be removed selectively to other materials. In one embodiment, a low power PECVD process, e.g., one taking place at less than about 200 Watts, is used.

In one embodiment, hydrogen bromide (“HBr”) and chlorine (“CI₂”) gases are fed into the reactor at appropriate flow rates to ensure that a plasma generated from those gases will modify exposed part 174 in the desired manner. Between about 50 and about 100 Watts wafer bias (for example, about 100 Watts) may be applied for a sufficient time to complete the desired transformation of exposed part 174. Plasma exposure lasting less than about one minute, and perhaps as short as 5 seconds, may be adequate to cause that conversion.

After exposed part 174 has been modified, it may be removed. The presence of the added impurities enables that exposed part to be etched selectively to covered part 175 to generate the FIG. 1D structure. In one embodiment, exposed part 174 is removed by exposing it to a relatively strong acid, e.g., a halide based acid (such as hydrobromic or hydrochloric acid) or phosphoric acid. When a halide based acid is used, the acid preferably contains between about 0.5% and about 10% HBr or HCI by volume—and more preferably about 5% by volume. An etch process that uses such an acid may take place at or near room temperature, and last for between about 5 and about 30 minutes—although a longer exposure may be used if desired. When phosphoric acid is used, the acid may contain between about 75% and about 95% H₃PO₄ by volume. An etch process that uses such an acid may, for example, take place at between about 140° C. and about 180° C., and, in one embodiment, at about 160° C. When such an acid is used, the exposure step may last between about 30 seconds and about 5 minutes—and for about one minute for a 20 Angstrom thick film.

FIG. 1D represents an intermediate structure that may be formed when making a complementary metal oxide semiconductor (“CMOS”). That structure includes first part 101 and second part 102 of substrate 100 shown in FIG. 1E. Isolation region 103 separates first part 101 from second part 102. Isolation region 103 may comprise silicon dioxide, or other materials that may separate the transistor's active regions. First sacrificial layer 104 is formed on first high-k gate dielectric layer 105, and second sacrificial layer 106 is formed on second high-k gate dielectric layer 107. Hard masks 130, 131 are formed on sacrificial layers 104, 106.

After forming the FIG. 1D structure, spacers may be formed on opposite sides of sacrificial layers 104, 106. When those spacers comprise silicon nitride, they may be formed in the following way. First, a silicon nitride layer of substantially uniform thickness, for example, less than about 1000 Angstroms thick—is deposited over the entire structure, producing the structure shown in FIG. 1E. Conventional deposition processes may be used to generate that structure.

In one embodiment, silicon nitride layer 134 is deposited directly on substrate 100 and opposite sides of sacrificial layers 104, 106—without first forming a buffer oxide layer on substrate 100 and layers 104, 106. In alternative embodiments, however, such a buffer oxide layer may be formed prior to forming layer 134. Similarly, although not shown in FIG. 1E, a second oxide may be formed on layer 134 prior to etching that layer. If used, such an oxide may enable the subsequent silicon nitride etch step to generate an L-shaped spacer.

Silicon nitride layer 134 may be etched using a conventional process for anisotropically etching silicon nitride to create the FIG. 1F structure. As a result of that etch step, sacrificial layer 104 is bracketed by a pair of sidewall spacers 108, 109, and sacrificial layer 106 is bracketed by a pair of sidewall spacers 110, 111.

As is typically done, it may be desirable to perform multiple masking and ion implantation steps to create lightly implanted regions 135 a-138 a near layers 104, 106 (that will ultimately serve as tip regions for the device's source and drain regions), prior to forming spacers 108, 109, 110, 111 on sacrificial layers 104, 106. Also, as it typically done, the source and drain regions 135-138 may be formed, after forming spacers 108, 109, 110, 111, by implanting ions into parts 101 and 102 of substrate 100, followed by applying an appropriate anneal step.

When sacrificial layers 104, 106 comprise polysilicon, an ion implantation and anneal sequence used to form n-type source and drain regions within part 101 of substrate 100 may dope polysilicon layer 104 n-type at the same time. Similarly, an ion implantation and anneal sequence used to form p-type source and drain regions within part 102 of substrate 100 may dope polysilicon layer 106 p-type. When doping polysilicon layer 106 with boron, that layer should include that element at a sufficient concentration to ensure that a subsequent wet etch process, for removing n-type polysilicon layer 104, will not remove a significant amount of p-type polysilicon layer 106.

The anneal will activate the dopants that were previously introduced into the source and drain regions and tip regions and into sacrificial layers 104, 106. In a preferred embodiment, a rapid thermal anneal is applied that takes place at a temperature that exceeds about 1,000° C.—and, optimally, that takes place at 1,080° C. In addition to activating the dopants, such an anneal may modify the molecular structure of high-k gate dielectric layers 105, 107 to create gate dielectric layers that may demonstrate improved performance.

Because of the imposition of the sacrificial metal layer 169, better performing dielectric layers 170 may result from these high temperature steps without significant reaction between the high dielectric constant dielectric layer 170 and the polysilicon layer 171.

After forming spacers 108, 109, 110, 111, dielectric layer 112 may be deposited over the device, generating the FIG. 1G structure. Dielectric layer 112 may comprise silicon dioxide, or a low-k material. Dielectric layer 112 may be doped with phosphorus, boron, or other elements, and may be formed using a high density plasma deposition process. By this stage of the process, source and drain regions 135, 136, 137, 138, which are capped by silicided regions 139, 140, 141, 142, have already been formed. Those source and drain regions may be formed by implanting ions into the substrate, then activating them. Alternatively, an epitaxial growth process may be used to form the source and drain regions, as will be apparent to those skilled in the art.

Forming sacrificial layers 104, 106 from polysilicon may enable one to apply commonly used nitride spacer, source/drain, and silicide formation techniques to make the FIG. 1G structure. That structure may include other features—not shown, so as not to obscure the method of the present invention—that may be formed using conventional process steps.

Dielectric layer 112 is removed from hard masks 130, 131, which are, in turn, removed from patterned sacrificial layers 104, 106, producing the FIG. 1H structure. conventional chemical mechanical polishing (“CMP”) operation may be applied to remove that part of dielectric layer 112 and hard masks 130, 131. Hard masks 130, 131 may be removed to expose patterned sacrificial layers 104, 106. Hard masks 130, 131 may be polished from the surface of layers 104, 106, when dielectric layer 112 is polished—as they will have served their purpose by that stage in the process.

After forming the FIG. 1H structure, sacrificial layer 104 is removed to generate trench 113 that is positioned between sidewall spacers 108, 109—producing the structure shown in FIG. 11. In one embodiment, a wet etch process that is selective for layers 104 over sacrificial layer 106 is applied to remove layers 104 and 169 without removing significant portions of layer 106.

When sacrificial layer 104 is doped n-type, and sacrificial layer 106 is doped p-type (e.g., with boron), such a wet etch process may comprise exposing sacrificial layer 104 to an aqueous solution that comprises a source of hydroxide for a sufficient time at a sufficient temperature to remove substantially all of layer 104. That source of hydroxide may comprise between about 2 and about 30 percent ammonium hydroxide or a tetraalkyl ammonium hydroxide, e.g., tetramethyl ammonium hydroxide (“TMAH”), by volume in deionized water.

Sacrificial layer 104 may be selectively removed by exposing it to a solution, which is maintained at a temperature between about 15° C. and about 90° C. (for example, below about 40° C.), that comprises between about 2 and about 30 percent ammonium hydroxide by volume in deionized water. During that exposure step, which preferably lasts at least one minute, it may be desirable to apply sonic energy at a frequency of between about 10 kHz and about 2,000 kHz, while dissipating at between about 1 and about 10 Watts/cm².

In one embodiment, sacrificial layer 104, with a thickness of about 1,350 Angstroms, may be selectively removed by exposing it at about 25° C. for about 30 minutes to a solution that comprises about 15 percent ammonium hydroxide by volume in deionized water, while applying sonic energy at about 1,000 kHz—dissipating at about 5 Watts/cm². Such an etch process should remove substantially all of an n-type polysilicon layer without removing a meaningful amount of a p-type polysilicon layer.

As an alternative, sacrificial layer 104 may be selectively removed by exposing it for at least one minute to a solution, which is maintained at a temperature between about 60° C. and about 90° C., that comprises between about 20 and about 30 percent TMAH by volume in deionized water, while applying sonic energy. Removing sacrificial layer 104, with a thickness of about 1,350 Angstroms, by exposing it at about 80° C. for about 2 minutes to a solution that comprises about 25 percent TMAH by volume in deionized water, while applying sonic energy at about 1,000 kHz—dissipating at about 5 Watts/cm²—may remove substantially all of layer 104 without removing a significant amount of layer 106. First high-k gate dielectric layer 105 should be sufficiently thick to prevent the etchant that is applied to remove sacrificial layer 104 from reaching the channel region that is located beneath first high-k gate dielectric layer 105.

The sacrificial metal layer 169 may also be removed by selective etching. In some embodiments, the layer 169 may not be removed.

In the illustrated embodiment, n-type metal layer 115 is formed directly on layer 105 to fill trench 113 and to generate the FIG. 1J structure. N-type metal layer 115 may comprise any n-type conductive material from which a metal NMOS gate electrode may be derived. N-type metal layer 115 preferably has thermal stability characteristics that render it suitable for making a metal NMOS gate electrode for a semiconductor device.

Materials that may be used to form n-type metal layer 115 include: hafnium, zirconium, titanium, tantalum, aluminum, and their alloys, e.g., metal carbides that include these elements, i.e., hafnium carbide, zirconium carbide, titanium carbide, tantalum carbide, and aluminum carbide. N-type metal layer 115 may be formed on first high-k gate dielectric layer 105 using well known PVD or CVD processes, e.g., conventional sputter or atomic layer CVD processes. As shown in FIG. 1K, n-type metal layer 115 is removed except where it fills trench 113. Layer 115 may be removed from other portions of the device via a wet or dry etch process, or an appropriate CMP operation. Dielectric 112 may serve as an etch or polish stop, when layer 115 is removed from its surface.

N-type metal layer 115 may serve as a metal NMOS gate electrode that has a workfunction that is between about 3.9 eV and about 4.2 eV, and that is between about 100 Angstroms and about 2,000 Angstroms thick and, in one embodiment, may particularly be between about 500 Angstroms and about 1,600 Angstroms thick. Although FIGS. 1J and 1K represent structures in which n-type metal layer 115 fills all of trench 113, in alternative embodiments, n-type metal layer 115 may fill only part of trench 113, with the remainder of the trench being filled with a material that may be easily polished, e.g., tungsten, aluminum, titanium, or titanium nitride. Using a higher conductivity fill metal in place of the workfunction metal may improve the overall conductivity of the gate stack. In such an alternative embodiment, n-type metal layer 115, which serves as the workfunction metal, may be between about 50 and about 1,000 Angstroms thick and, for example, at least about 100 Angstroms thick.

In embodiments in which trench 113 includes both a workfunction metal and a trench fill metal, the resulting metal NMOS gate electrode may be considered to comprise the combination of both the workfunction metal and the trench fill metal. If a trench fill metal is deposited on a workfunction metal, the trench fill metal may cover the entire device when deposited, forming a structure like the FIG. 1J structure. That trench fill metal must then be polished back so that it fills only the trench, generating a structure like the FIG. 1K structure.

In the illustrated embodiment, after forming n-type metal layer 115 within trench 113, sacrificial layer 106 is removed to generate trench 150 that is positioned between sidewall spacers 110, 111—producing the structure shown in FIG. 1L. In a preferred embodiment, layer 106 is exposed to a solution that comprises between about 20 and about 30 percent TMAH by volume in deionized water for a sufficient time at a sufficient temperature (e.g., between about 60° C. and about 90° C.), while applying sonic energy, to remove all of layer 106 without removing significant portions of n-type metal layer 115.

Alternatively, a dry etch process may be applied to selectively remove layer 106. When sacrificial layer 106 is doped p-type (e.g., with boron), such a dry etch process may comprise exposing sacrificial layer 106 to a plasma derived from sulfur hexafluoride (“SF₆”), hydrogen bromide (“HBr”), hydrogen iodide (“HI”), chlorine, argon, and/or helium. Such a selective dry etch process may take place in a parallel plate reactor or in an electron cyclotron resonance etcher.

After removing sacrificial layer 106, it may be desirable to clean second high-k gate dielectric layer 107, e.g., by exposing that layer to the hydrogen peroxide based solution described above. Optionally, as mentioned above, a capping layer (which may be oxidized after it is deposited) may be formed on second high-k gate dielectric layer 107 prior to filling trench 150 with a p-type metal. In this embodiment, however, p-type metal layer 116 is formed directly on layer 107 to fill trench 150 and to generate the FIG. 1M structure. P-type metal layer 116 may comprise any p-type conductive material from which a metal PMOS gate electrode may be derived. P-type metal layer 116 preferably has thermal stability characteristics that render it suitable for making a metal PMOS gate electrode for a semiconductor device.

Materials that may be used to form p-type metal layer 116 include: ruthenium, palladium, platinum, cobalt, nickel, and conductive metal oxides, e.g., ruthenium oxide. P-type metal layer 116 may be formed on second high-k gate dielectric layer 107 using well known PVD or CVD processes, e.g., conventional sputter or atomic layer CVD processes. As shown in FIG. 1N, p-type metal layer 116 is removed except where it fills trench 150. Layer 116 may be removed from other portions of the device via a wet or dry etch process, or an appropriate CMP operation, with dielectric 112 serving as an etch or polish stop.

P-type metal layer 116 may serve as a metal PMOS gate electrode with a workfunction that is between about 4.9 eV and about 5.2 eV, and that is between about 100 angstroms and about 2,000 angstroms thick, and more preferably is between about 500 angstroms and about 1,600 angstroms thick. Although FIGS. 1M and 1N represent structures in which p-type metal layer 116 fills all of trench 150, in alternative embodiments, p-type metal layer 116 may fill only part of trench 150. As with the metal NMOS gate electrode, the remainder of the trench may be filled with a material that may be easily polished, e.g., tungsten, aluminum, titanium, or titanium nitride. In such an alternative embodiment, p-type metal layer 116, which serves as the workfunction metal, may be between about 50 and about 1,000 angstroms thick. Like the metal NMOS gate electrode, in embodiments in which trench 150 includes a workfunction metal and a trench fill metal, the resulting metal PMOS gate electrode may be considered to comprise the combination of both the workfunction metal and the trench fill metal.

After removing metal layer 116, except where it fills trench 150, a capping dielectric layer may be deposited onto dielectric layer 112, metal NMOS gate electrode 115, and metal PMOS gate electrode 116, using any conventional deposition process. Process steps for completing the device that follow the deposition of such a capping dielectric layer, e.g., forming the device's contacts, metal interconnect, and passivation layer, are well known to those skilled in the art and will not be described here.

Although the embodiment described above anneals high-k gate dielectric layers 105, 107 when dopants—previously implanted into sacrificial layers 104, 106 and into the source and drain regions—are activated, the high-k gate dielectric layer (or layers) may be annealed at a different stage in the process. For example, a high temperature anneal may be applied to high-k gate dielectric layer 170 immediately after that layer has been deposited on substrate 100, or such an anneal may be applied immediately after high-k gate dielectric layer 170 has been etched to form high-k gate dielectric layers 105, 107. The temperature at which such an anneal takes place should exceed about 700° C.

Forming high-k gate dielectric layers 105, 107 prior to removing sacrificial layers 104, 106 enables a high temperature anneal to be applied to those dielectric layers prior to forming silicided regions, and prior to forming metal layers on high-k gate dielectric layers 105, 107. Forming high-k gate dielectric layers 105, 107 at a relatively early stage in the process is advantageous for another reason. When an atomic layer CVD process is applied to generate high-k gate dielectric layers at the bottom of trenches 113, 150—after sacrificial layers 104, 106 are removed, the high-k dielectric material may be deposited on both the sides and bottoms of the trenches. Additional process steps may be required to prevent the high-k dielectric material's presence on the sides of the trenches from adversely affecting device characteristics—complicating the overall process. Forming high-k gate dielectric layers 105, 107 prior to removing sacrificial layers 104, 106, ensures that the high-k dielectric material will form on the trench bottoms only, and not on the sides of the trenches.

The method described above enables production of CMOS devices that include high-k gate dielectric layers, which have been subjected to a high temperature anneal. This method enables such an anneal to be applied to such a dielectric layer without damaging any silicide or high temperature intolerant metal that may be used to make the device's transistors.

While the present invention has been described with respect to a limited number of embodiments, those skilled in the art will appreciate numerous modifications and variations therefrom. It is intended that the appended claims cover all such modifications and variations as fall within the true spirit and scope of this present invention. 

1. A method comprising: covering a gate dielectric with a sacrificial metal layer; and depositing a polysilicon layer over said sacrificial metal layer; exposing said gate dielectric to a temperature greater than 450° C. while covered with said sacrificial metal layer and said polysilicon layer; patterning and etching said polysilicon layer to form a gate electrode; and removing said polysilicon gate electrode and said sacrificial metal layer.
 2. The method of claim 1 including covering the gate dielectric with a metal nitride sacrificial metal layer.
 3. The method of claim 2 including covering the gate dielectric with a titanium nitride layer.
 4. The method of claim 1 including replacing said polysilicon gate electrode with a metal gate electrode.
 5. The method of claim 1 including sputtering said sacrificial metal layer on said gate dielectric.
 6. A method comprising: covering a gate dielectric with a sacrificial metal layer; depositing a polysilicon layer over said sacrificial metal layer; patterning and etching NMOS and PMOS stacks from said polysilicon layer, said gate dielectric, and said sacrificial metal layer; exposing said stacks to a temperature greater than 450° C.; covering the gate dielectric with a metal nitride sacrificial metal layer; covering the gate dielectric with a titanium nitride layer; and removing said polysilicon layers and said sacrificial metal layers of said stacks.
 7. The method of claim 6 including replacing said polysilicon layers with a metal gate electrode.
 8. The method of claim 6 including using sputtering to cover said gate dielectric with a sacrificial metal layer. 